Mehrschicht-Ferrit-Chip-Induktor (ML-Serie ML03MTR39)Hersteller

Mehrschicht-Ferrit-Chip-Induktor (ML-Serie ML03MTR39)

ML03MTR39

Mehrschicht-Ferrit-Chip-Induktor (ML-Serie ML03MTR39) Files Download

Mehrschicht-Ferrit-Chip-Induktor, kleine Größen, geschlossener magnetischer Kreis vermeidet Übersprechen, geeignet für eine hohe Dichte an Installationen und Reflow-Löten. Verwendet in allen Arten von elektronischen Geräten, Computern, Wandlern.
ML Series0603 ±20%nH 390μH 1 Ω 35mA 15 110MHz 25MHz, 200mV MHz

Größe	Toleranz	Induktivität	DCR (Ω) max.	IDC (mA)	Q	SRF	L/Q Frequenz (MHz)
0603	±20%	390	1	35	15	110MHz	25MHz, 200mV

Hoher Strom Elektrische Spezifikationen

MLH05 Multilayer Ferrite Chip Inductors Type(□:Tolerance):

Part No.	Inductance (uH)	Tolerance	Test Freq.	SRF (MHz) min.	DCR (Ω) max.	IDC (mA) max.
MLH05□TR47	0.47	± 20%	1MHz, 250mV	100	0.125	1100
MLH05□TR68	0.68	± 20%	1MHz, 250mV	100	0.150	1000
MLH05□TR82	0.82	± 20%	1MHz, 250mV	90	0.175	900
MLH05□T1R0	1.0	± 20%	1MHz, 250mV	90	0.200	800
MLH05□T1R2	1.2	± 20%	1MHz, 250mV	80	0.200	800
MLH05□T1R5	1.5	± 20%	1MHz, 250mV	70	0.275	700
MLH05□T1R8	1.8	± 20%	1MHz, 250mV	60	0.275	700
MLH05□T2R2	2.2	± 20%	1MHz, 250mV	50	0.313	600
MLH05□T3R3	3.3	± 20%	1MHz, 250mV	40	0.275	500
MLH05□T4R7	4.7	± 20%	1MHz, 250mV	30	0.375	500

☑ Operating temperature range: -40 ~ +125°C

MLH06 Multilayer Ferrite Chip Inductors Type(□:Tolerance):

Part No.	Inductance (uH)	Tolerance	Test Freq.	SRF (MHz) min.	DCR (Ω) max.	IDC (mA) max.
MLH06□TR47	0.47	± 20%	1MHz, 250mV	100	0.182	1500
MLH06□TR68	0.68	± 20%	1MHz, 250mV	90	0.195	1500
MLH06□TR82	0.82	± 20%	1MHz, 250mV	80	0.208	1500
MLH06□T1R0	1.0	± 20%	1MHz, 250mV	60	0.208	1400
MLH06□T1R2	1.2	± 20%	1MHz, 250mV	60	0.208	1400
MLH06□T1R5	1.5	± 20%	1MHz, 250mV	50	0.260	1200
MLH06□T1R8	1.8	± 20%	1MHz, 250mV	50	0.260%	1200
MLH06□T2R2	2.2	± 20%	1MHz, 250mV	40	0.286	1200
MLH06□T3R3	3.3	± 20%	1MHz, 250mV	30	0.312	1100
MLH06□T4R7	4.7	± 20%	1MHz, 250mV	20	0.390	1100

☑ Operating temperature range: -40 ~ +125°C

MLH08 Multilayer Ferrite Chip Inductors Type(□:Tolerance):

Part No.	Inductance (uH)	Tolerance	Test Freq.	SRF (MHz) min.	DCR (Ω) max.	IDC (mA) max.
MLH08□TR47	0.47	± 20%	1MHz, 250mV	100	0.088	1800
MLH08□TR68	0.68	± 20%	1MHz, 250mV	90	0.113	1700
MLH08□TR82	0.82	± 20%	1MHz, 250mV	80	0.125	1700
MLH08□T1R0	1.0	± 20%	1MHz, 250mV	60	0.138	1600
MLH08□T1R2	1.2	± 20%	1MHz, 250mV	60	0.138	1600
MLH08□T1R5	1.5	± 20%	1MHz, 250mV	50	0.163	1500
MLH08□T1R8	1.8	± 20%	1MHz, 250mV	50	0.163	1500
MLH08□T2R2	2.2	± 20%	1MHz, 250mV	40	0.213	1300
MLH08□T3R3	3.3	± 20%	1MHz, 250mV	30	0.200	1200
MLH08□T4R7	4.7	± 20%	1MHz, 250mV	25	0.250	1100

☑ Operating temperature range: -40 ~ +125°C

Umwelteigenschaften

Electrical Performance Test

Item	Requirement	Test Method
Inductance	Refer to standard electrical characteristic spec.	HP4291B
Q		HP4291B
SRF		HP4291B
DC Resistance RDC		Agilent 34401A

Mechanical Performance Test

Item	Requirement	Test Method
Resistance to Soldering Heat	Appearance: No damage More than 75% of the terminal. Electrode should be covered with solder.	Pre-heating: 150°C, 1min. Solder Composition: Sn/Ag3.0/Cu0.5 (Pb-Free) Solder Temperature: 260± 5°C (Pb-Free) Immersion Time: 10± 1 sec.
Solderability	The electrodes shall be at least 90% covered with new solder coating	Pre-heating: 150°C, 1min. Solder Composition: Sn/Ag3.0/Cu0.5 (Pb-Free) Solder Temperature: 245± 5°C (Pb-Free) Immersion Time: 4± 1 sec.
Flexure Strength	The forces applied on the right conditions must not damage the terminal electrode and the ferrite.	Test device shall be soldered on the substrate Substrate Dimension: 100 x 40 x 1.6 mm Deflection: 2.0 mm Keeping Time: 30 sec. * For 0402, substrate dimension is 100 x 40 x 0.8 mm
Vibration		Test device shall be soldered on the substrate Oscillation Frequency: 10 to 55 to 10Hz for 1 min. Amplitude: 1.5 mm Time: 2 hrs for each axis (X, Y & Z), total 6 hrs

Climatic Test

Item

Requirement

Test Method

Damp Heat with Load

Appearance: No damage
L change: within± 20% of initial value

Temperature: 40± 2°C
Relative Humidity: 90 ~ 95%
Time: 1000 hrs
Measured after exposure in the room condition for 24 hrs

Temperature Cycle

One cycle:

Step	Temperature (°C)	Time (min.)
1	-40± 3	30
2	25± 2	3
3	85± 3	30
4	25± 2	3

Total: 100 cycles
Measured after exposure in the room condition for 24 hrs

High Temperature Resistance

Temperature: 85± 3°C
Relative Humidity: 20%
Applied Current: Rated Current
Time: 1000 hrs
Measured after exposure in the room condition for 24 hrs

Low Temperature Resistance

Temperature: -40± 3°C
Relative Humidity: 0%
Time: 1000 hrs
Measured after exposure in the room condition for 24 hrs

☑ Storage Temperature: 15 ~ 28°C; Humidity < 80%RH

Verpackung

Reel Specifications (Unit : mm)

Type	A	B	C	W	T	Quantity (EA)
Type	A	B	C	W	T	Paper Tape (Type B)	Polystyrene Tape (Type A)
ML03	178 ± 1	60.0 + 0.5	13.0 ± 0.2	9.00 ± 0.5	12.0 ± 0.15	4,000	-
ML05 (≤ 2.2uH)	178 ± 1	60.0 + 0.5	13.0 ± 0.2	9.00 ± 0.5	12.0 ± 0.15	4,000	-
ML05 (≥ 2.7uH)	178 ± 1	60.0 + 0.5	13.0 ± 0.2	9.00 ± 0.5	12.0 ± 0.15	-	3,000
ML06	178 ± 1	60.0 + 0.5	13.0 ± 0.2	9.00 ± 0.5	12.0 ± 0.15	-	3,000
MLH05	178 ± 1	60.0 + 0.5	13.0 ± 0.2	9.00 ± 0.5	12.0 ± 0.15	4.000	-
MLH06	178 ± 1	60.0 + 0.5	13.0 ± 0.2	9.00 ± 0.5	12.0 ± 0.15	-	3,000
MLH08	178 ± 1	60.0 + 0.5	13.0 ± 0.2	9.00 ± 0.5	12.0 ± 0.15	-	3,000

Tape Specifications & Tape Material (Unit : mm)

Type	A	B	T	W	P	F	K	Tape Type
ML03	1.05	1.85	0.95	8.0	4.0	3.5	-	B
ML05(≤ 2.2uH)	1.50	2.42	0.95	8.0	4.0	3.5	-	B
ML05(≥ 2.7uH)	1.50	2.35	1.45	8.0	4.0	3.5	0.22	A
ML06	1.88	3.50	1.27	8.0	4.0	3.5	0.22	A
MLH05	1.45	2.25	0.95	8.0	4.0	3.5	-	B
MLH06	1.88	2.40	1.23	8.0	4.0	3.5	0.23	A
MLH08	2.20	2.85	1.40	8.0	4.0	3.5	0.23	A

Note:
1. Please make sure that your product is has been evaluated and confirmed against your specifications when our product is mounted to your product.
2. Do not knock nor drop.
3. All the items and parameters in this product specification have been prescribed on the premise that our product is used for the purpose, under the condition and in the environment agreed upon between you and us. You are requested not to use our product deviating from such agreement.

Dateien herunterladen

Datenblatt
Mehrschicht-Ferrit-Chip-Induktor - ML-Serie

SUCHE

Bedingungssuche: Kreuzsuche

Bester Verkauf

Mehrschicht-Ferrit-Chip-Induktor (ML-Serie ML03MTR39)Hersteller - Viking

Mit Sitz in Taiwan ist Viking Tech Corporation seit 1997 einer der führenden Mehrschicht-Ferrit-Chip-Induktor (ML-Serie ML03MTR39) Hersteller.Und ihre Produkte werden in der gesamten Automobil- und Elektronikgeräteindustrie eingesetzt, mit einer Fertigungstoleranz von bis zu 0,01 % und einem TCR von bis zu 2 ppm in einer breiten Palette von Gehäusegrößen.

Mit TS16949/ ISO9001/ ISO14001 und Erfüllung der AEC-Q200-Standards bietet Viking antischwefelhaltige, überspannungsfeste, puls-, hochspannungs- und hochleistungsfähige Präzisionswiderstände, einschließlich Dünn-/Dickfilmwiderstände, Automobilwiderstände, Melf-Widerstände, Strommesswiderstände usw. Niedriges Rauschen, niedriger TC, Hochleistungsinduktoren wie RF-Induktoren, Chip-Induktoren, Leistungsinduktoren, variable Induktoren, Ferrit-Chip-Induktoren, geschirmte Induktoren, Drahtwickelinduktoren und DIP-Induktoren.

Mehrschicht-Ferrit-Chip-Induktor (ML-Serie ML03MTR39)bietet Kunden seit vielen Jahren hochwertige Leistungswiderstände, Leistungsdrosseln und Aluminium-Elektrolytkondensatoren mit einem soliden Ruf an. Mit fortschrittlicher Technologie und 25 Jahren Erfahrung stellt Viking sicher, dass alle Kundenanforderungen erfüllt werden.